Spesifikasi:
| Nama Produk | 301 Kumparan / strip baja tahan karat |
| Proses | Gulungan Panas / Gulungan Dingin |
| Nilai | Seri 200/300/400 (301 310s 309s 304 316 316l 201 202 321 410 430 ......) |
| Permukaan | No.1/ 2B/ BA/No.4/ HL |
| Standar | AISI ASTM JIS EN DIN ...... |
| Ketebalan | 0.2-3mm (digulung dingin) 3-6mm (digulung panas) |
| Lebar | 5mm ~ 600mm |
Komposisi kimia:
|
Elemen |
Persentase Berat Maksimum Kecuali Rentang Ditentukan |
| Karbon | 0,15 maksimum |
| Mangan | 2.00 maksimum |
| Fosfor | 0,045 maksimum |
| Sulfur | 0,030 maksimum |
| silikon | 0,75 maksimum |
| kromium | 16.00-18.00 |
| Nikel | 6.00-8.00 |
| Nitrogen | 0,10 maksimum |
Peralatan mekanis:
| Kondisi |
Daya tarik, min.Ksi(MPa) |
Kekuatan Hasil 0,2%, min.Ksi (MPa) |
memanjang.Dalam 2" (50mm) %, Min. |
||
| anil | 75 | 515 | 30 | 205 | 40 |
| 1/4 Keras | 125 | 862 | 75 | 517 | 25 |
| 1/2 Keras | 150 | 1,034 | 110 | 758 | 18 |
| 3/4 Keras | 175 | 1,207 | 125 | 931 | 12 |
| Penuh Keras | 185 | 1,276 | 140 | 965 | 9 |
marah:
|
Melunakkan |
Kondisi |
Ketegangan | ||||||||||
| Membujur | Melintang | |||||||||||
|
0,2% YS Ksi (MPa) |
Modulus 10 6psi (GPa) |
0,2% YS Ksi (MPa) |
Modulus 10 6psi (GPa) |
|||||||||
|
anil 1/4 Keras |
sebagai anil Saat digulung Stres lega |
36 80 77 |
(248) (552) (531) |
31.0 28.0 28.7 |
(214) (193) (198) |
36 84 79 |
(248) (579) (545) |
30.6 28.6 27.0 |
(211) (197) (186) |
|||
| 1/2 Keras | Saat digulung Stres lega |
122 128 |
(841) (883) |
26.8 27.9 |
(185) (192) |
123 130 |
(848) (896) |
28.1 28.6 |
(194) (197) |
|||
| 3/4 Keras | Saat digulung Stres lega |
142 155 |
(979) (1.069) |
25.8 27.3 |
(178) (188) |
145 155 |
(1.000) (1.069) |
27.5 28.8 |
(190) (199) |
|||
| Penuh Keras | Saat digulung Stres lega |
160 175 |
(1.103) (1.207) |
25.2 28.4 |
(174) (196) |
163 181 |
(1,124) (1.248) |
28.4 30.5 |
(196) (210) |
|||
| Kompresi | ||||||||||||
|
anil 1/4 Keras |
sebagai anil Saat digulung Stres lega |
38 50 73 |
(262) (345) (503) |
30.6 28.2 28.8 |
(211) (194) (199) |
38 91 84 |
(262) (627) (579) |
30.3 28.2 30.6 |
(209) (194) (211) |
|||
| 1/2 Keras | Saat digulung Stres lega |
90 111 |
(621) (765) |
27.5 29.2 |
(190) (201) |
142 144 |
(979) (993) |
27.5 29.8 |
(190) (205) |
|||
| 3/4 Keras | Saat digulung Stres lega |
100 133 |
(690) (917) |
26,5 27.5 |
(183) (190) |
170 176 |
(1.172) (1.213) |
27.9 29.5 |
(192) (203) |
|||
| Penuh Keras | Saat digulung Stres lega |
115 169 |
(793) (1,165) |
24.6 27.7 |
(170) (191) |
191 209 |
(1.317) (1.441) |
29.4 29.6 |
(203) (204) |
|||